http://join2-wiki.gsi.de/foswiki/pub/Main/Artwork/join2_logo100x88.png HTS Nuclotron Cable Produced [IFAST-MS36 Milestone Report]

Gömöry, F. ; Dhallé, M. ; Kade, A. (Contributor) ; Winkler, T. (Contributor)GSI*

2023
Zenodo

Please use a persistent id in citations: doi:10.5281/ZENODO.7995185

Report No.: Zenodo:7995185

Abstract: Two samples of the Nuclotron CORT cable were manufactured and tested for their magnetization loss. The cables were designed to have a critical current of 1350 A at 77.3 K and around 10 kA at 4.2 K. The cable was made using commercial REBCO coated conductor from a non-European manufacturer, which had excellent mechanical properties. The experiments were conducted at IEE Bratislava and at University of Twente in Enschede at 77.3 K and 4.2 K, respectively. The results confirm the expectation that there are negligible electrical contacts between the copper-stabilized tape strands and that it is possible to estimate hysteresis loss analytically for accelerator-magnet-relevant operating conditions.

---

Contributing Institute(s):

1. SC Magnets & Testing (SCM)

Research Program(s):

1. 621 - Accelerator Research and Development (POF4-621) (POF4-621)
2. I.FAST - Innovation Fostering in Accelerator Science and Technology (101004730) (101004730)

Experiment(s):

1. External experiment at external facility/ no experiment at GSI (other)

Appears in the scientific report 2023

---